Stress-generating structure for semiconductor-on-insulator devices

ABSTRACT

A stack pad layers including a first pad oxide layer, a pad nitride layer, and a second pad oxide layer are formed on a semiconductor-on-insulator (SOI) substrate. A deep trench extending below a top surface or a bottom surface of a buried insulator layer of the SOI substrate and enclosing at least one top semiconductor region is formed by lithographic methods and etching. A stress-generating insulator material is deposited in the deep trench and recessed below a top surface of the SOI substrate to form a stress-generating buried insulator plug in the deep trench. A silicon oxide material is deposited in the deep trench, planarized, and recessed. The stack of pad layer is removed to expose substantially coplanar top surfaces of the top semiconductor layer and of silicon oxide plugs. The stress-generating buried insulator plug encloses, and generates a stress to, the at least one top semiconductor region.

This application is a divisional application of U.S. Ser. No.11/860,851, filed on Sep. 25, 2007. The entire contents of each of theaforementioned U.S. Application are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention generally relates to semiconductor structures, andparticularly to stress-generating structures forsemiconductor-on-insulator (SOI) devices and methods of manufacturingthe same.

BACKGROUND OF THE INVENTION

When stress is applied to the channel within an active area of asemiconductor transistor, the mobility of carriers, and as aconsequence, the transconductance and the on-current of the transistorare altered from their corresponding values for a transistor containingan unstressed semiconductor. This is because the applied stress and theresulting strain on the semiconductor structure within the channelaffects the band gap structure (i.e., breaks the degeneracy of the bandstructure) and changes the effective mass of carriers. The effect of thestress depends on the crystallographic orientation of the plane of thechannel, the direction of the channel within the crystallographicorientation, the direction of the applied stress, and the type ofcarries.

The effect of stress on the performance of semiconductor devices,especially on the performance of a metal-oxide-semiconductor fieldeffect transistor (MOSFET, or a “FET” in short) device built on asilicon substrate, has been extensively studied in the semiconductorindustry. For a p-type MOSFET (PMOSFET, or a “PFET” in short) utilizinga silicon channel, the mobility of minority carriers in the channel(which are holes in this case) increases under uniaxial compressivestress along the direction of the channel, i.e., the direction of themovement of holes or the direction connecting the drain to the source.Conversely, for an n-type MOSFET (NMOSFET, or an “NFET” in short)devices utilizing a silicon channel, the mobility of minority carriersin the channel (which are electrons in this case) increases underuniaxial tensile stress along the direction of the channel, i.e., thedirection of the movement of electrons or the direction connecting thedrain to the source. Tensile stress in transverse direction, i.e., thedirection perpendicular to the movement of carries, can enhance bothelectron and hole mobilities. Thus, performance of field effecttransistors may be improved by forming a stress-generating structure inor on a semiconductor substrate.

Methods of employing stress-generating shallow trench isolation linersin a bulk substrate are known in the art. Direct application of suchmethods to semiconductor-on-insulator substrate results in aninsignificant amount of improvement in performance compared to bulkequivalents. This is because the thickness of a top semiconductor layeris much less than a depth of shallow trench isolation in bulksubstrates, which may be from about 300 nm to about 450 nm, and theamount of stress transferred to SOI devices is proportional to thethickness of the top semiconductor layer, which may be from about 5 nmto about 30 nm in the case of ultra-thin semiconductor-on-insulator(UTSOI) substrates employed for high performance devices.

In view of the above, there exists a need for an effectivestress-generating structure for semiconductor-on-insulator (SOI)devices, and methods of manufacturing the same.

Further, current semiconductor processing sequence used in industryemploys silicon oxide as a trench fill material. Modification of anexposed structure of the trench isolation structure would requirealterations to subsequent processing steps.

Therefore, there exists a need for an effective stress-generatingstructure that is compatible with existing semiconductor processingafter formation of trench isolation structures, and methods ofmanufacturing the same.

SUMMARY OF THE INVENTION

The present invention addresses the needs described above by providing astress-generating structure which is compatible withsemiconductor-on-insulator substrates and existing processing afterformation of trench isolation structures, and methods of manufacturingthe same.

In the present invention, a stack of pad layers including a first padoxide layer, a pad nitride layer, and a second pad oxide layer areformed on a semiconductor-on-insulator (SOI) substrate. A deep trenchextending below a bottom surface of a buried insulator layer of the SOIsubstrate and enclosing at least one top semiconductor region is formedby lithographic methods and etching. A stress-generating nitridematerial is deposited in the deep trench and recessed below a topsurface of the SOI substrate to form a stress-generating buried nitrideplug in the deep trench. A silicon oxide material is deposited in thedeep trench, planarized, and recessed. The stack of pad layers isremoved to expose substantially coplanar top surfaces of the topsemiconductor layer and of silicon oxide plugs. The stress-generatingburied nitride plug encloses, and generates either a compressive stressor tensile stress to, the at least one top semiconductor region.

According to an aspect of the present invention, a semiconductorstructure is provided which comprises:

a semiconductor-on-insulator (SOI) substrate including a handlesubstrate, at least one buried insulator portion abutting the handlesubstrate, and at least one top semiconductor portion abutting the atleast one buried insulator portion;

a trench extending from a top surface of the at least one topsemiconductor portion to a depth below a top surface of the at least oneburied insulator portion; and

a stack of an insulator stressor plug and a silicon oxide plug locatedin the trench, wherein the insulator stressor plug abuts a bottomsurface of the trench and the silicon oxide plug is substantiallycoplanar with the top surface of the at least one top semiconductorportion.

In one embodiment, the trench extends a depth below a bottom surface ofthe at least one buried insulator portion.

In another embodiment, the insulator stressor plug comprises a siliconnitride and applies a tensile stress or a compressive stress to the atleast one top semiconductor portion.

In even another embodiment, a magnitude of the tensile stress or thecompressive stress is greater than 0.2 GPa in a region in the at leastone top semiconductor portion.

In yet another embodiment, the insulator stressor plug laterally abuts,and encloses, the at least one buried insulator portion.

In still another embodiment, the insulator stressor plug laterally abutsand encloses the at least one top semiconductor portion.

In still yet another embodiment, an interface between the insulatorstressor plug and the silicon oxide plug is located between the topsurface of the at least one top semiconductor portion and a bottomsurface of the at least one top semiconductor portion, or at the bottomsurface of the at least one top semiconductor portion.

In a further embodiment, an interface between the insulator stressorplug and the silicon oxide plug is located between a top surface of theat least one buried insulator portion and the bottom surface of the atleast one buried insulator portion, or at the bottom surface of the atleast one buried insulator portion.

In an even further embodiment, an interface between the insulatorstressor plug and the silicon oxide plug is located beneath the bottomsurface of the at least one buried insulator portion.

In a yet further embodiment, the at least one top semiconductor layercomprises one of silicon, germanium, a silicon germanium alloy, asilicon carbon alloy, and a silicon germanium carbon alloy.

In a still further embodiment, a thickness of the at least one topsemiconductor portion is from about 5 nm to about 300 nm, and wherein adepth of the trench is from about 200 nm to about 8,000 nm.

According to another aspect of the present invention, a method offorming a semiconductor structure is provided, which comprises:

forming a trench extending from a top surface of asemiconductor-on-insulator (SOI) substrate to a depth beneath a bottomsurface of a buried insulator layer of the SOI substrate; and

forming a stack of an insulator stressor plug and a silicon oxide plugin the trench, wherein the insulator stressor plug abuts a bottomsurface of the trench, and wherein the silicon oxide plug issubstantially coplanar with a top surface of at least one topsemiconductor portion formed in a top semiconductor layer of the SOIsubstrate.

In one embodiment, the method further comprises:

forming a stack of pad layers directly on the SOI substrate;

applying a photoresist on the stack of pad layers and lithographicallypatterning the photoresist; and

transferring a pattern in the resist into the stack of pad layers andthe SOI substrate by at least one reactive etch.

In another embodiment, the trench laterally abuts and encloses the atleast one top semiconductor portion and at least one buried insulatorportion, wherein the at least one buried insulator portion verticallyabuts the at least one top semiconductor portion.

In yet another embodiment, the method further comprises:

depositing a silicon nitride into the trench; and recessing the siliconnitride in the trench to form the insulator stressor plug.

In still another embodiment, the insulator stressor plug comprises asilicon nitride and applies a compressive stress or a tensile stress tothe at least one top semiconductor portion.

In still yet another embodiment, a magnitude of the tensile stress orthe compressive stress exceeds 0.2 GPa in a region in the at least onetop semiconductor portion.

In a further embodiment, the method further comprises:

depositing a silicon oxide into the trench on top of the insulatorstressor plug; and

recessing the silicon oxide in the trench to form the silicon oxideplug.

In an even further embodiment, an interface between the insulatorstressor plug and the silicon oxide plug is located between the topsurface of the at least one top semiconductor portion and a bottomsurface of the at least one top semiconductor portion, or at the bottomsurface of the at least one top semiconductor portion.

In a yet further embodiment, an interface between the insulator stressorplug and the silicon oxide plug is located between a top surface of theburied insulator layer and the bottom surface of the buried insulatorlayer, or at the bottom surface of the buried insulator layer.

In a still further embodiment, a thickness of the at least one topsemiconductor portion is from about 5 nm to about 300 nm, and wherein adepth of the trench is from about 200 nm to about 8,000 nm.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-3, 5-11 are sequential vertical cross-sectional views of a firstexemplary semiconductor structure according to the present invention.FIG. 4 is a top-down view of the exemplary semiconductor structure inFIG. 4. FIG. 12 is a top-down view of the exemplary semiconductorstructure in FIG. 11. FIG. 13 is a horizontal cross-sectional view ofthe exemplary semiconductor structure in FIG. 11 along the plane X-X′.

Each of FIGS. 14-15 is a superposition of FIG. 11 with a stressschematic indicating the direction of stress generated by astress-generating nitride plug.

FIG. 16 is a vertical cross-sectional view of a second exemplarysemiconductor structure according to the present invention.

FIG. 17 is a vertical cross-sectional view of a third exemplarysemiconductor structure according to the present invention.

FIG. 18 is a two-dimensional model for simulation of stress in a fourthexemplary semiconductor structure according to the present invention.

FIG. 19 is a plot of lateral stress from a simulation employing thetwo-dimensional model of FIG. 15.

DETAILED DESCRIPTION OF THE INVENTION

As stated above, the present invention relates to particularly tostress-generating structures for semiconductor-on-insulator (SOI)devices and methods of manufacturing the same, which are now describedin detail with accompanying figures. It is noted that like andcorresponding elements are referred to by like reference numerals.

Referring to FIG. 1, a vertical cross-sectional view of a firstexemplary semiconductor structure is shown, which comprises asemiconductor-on-insulator (SOI) substrate 8 containing a handlesubstrate 10, a buried insulator layer 20, and a top semiconductor layer30. The handle substrate 10 may comprise a semiconductor material suchas silicon. Preferably, the handle substrate 10 comprises a singlecrystalline semiconductor material. The handle substrate 10 may have ap-type doping or an n-type doping. The conductivity of the doping of thehandle substrate 10 is herein referred to as a first conductivity type.The dopant concentration of the handle substrate 10 is from about1.0×10¹⁴/cm³ to about 3.0×10¹⁷/cm³, and typically at a dopantconcentration from about 1.0×10¹⁵/cm³ to about 3.0×10¹⁶/cm³. The buriedinsulator layer 20 comprises a dielectric material such as a siliconoxide or a silicon nitride. Preferably, the buried insulator layer 20comprises thermal silicon oxide. The thickness of the buried insulatorlayer 20 may be from about 50 nm to about 400 nm, and typically fromabout 100 nm to about 200 nm. Implementation of the present invention ona hybrid substrate containing a bulk portion and an SOI portion isexplicitly contemplated herein.

The top semiconductor layer 30 comprises a semiconductor material thatmay be selected from, but is not limited to, silicon, germanium,silicon-germanium alloy, silicon carbon alloy, silicon-germanium-carbonalloy, gallium arsenide, indium arsenide, indium phosphide, III-Vcompound semiconductor materials, II-VI compound semiconductormaterials, organic semiconductor materials, and other compoundsemiconductor materials. The thickness of the top semiconductor layer 30may be from about 5 nm to about 300 nm, and preferably from about 5 nmto about 100 nm. Preferably, the entirety of the top semiconductor layer30 comprises a single crystalline semiconductor material.

The top semiconductor layer 30 may have a built-in biaxial stress in theplane of the top semiconductor layer 30, i.e., in the planeperpendicular to the direction of the surface normal of a substrate topsurface 29, which is a top surface of the SOI substrate 8. The topsemiconductor layer 30 may be substantially undoped of may have a dopingof the first conductivity type or a doping of the opposite type of thefirst conductivity type, which is herein referred to as a secondconductivity type. The dopant concentration of the top semiconductorlayer 30 may be from about 1.0×10¹⁴/cm³ to about 3.0×10¹⁷/cm³, andtypically from about 1.0×10¹⁵/cm³ to about 3.0×10¹⁶/cm³, although lesserand greater dopant concentrations are explicitly contemplated herein.

Referring to FIG. 2, a stack of pad layers is formed on the substratetop surface 29. Specifically, a first pad oxide layer 40 is formeddirectly on the substrate top surface. The first pad oxide layer 40 maycomprise a thermal oxide of the semiconductor material in the topsemiconductor layer 30, or may comprise a dielectric oxide materialdeposited by chemical vapor deposition (CVD). The first pad oxide layer30 may comprise a silicon oxide such as a thermal silicon oxide or adeposited silicon oxide formed by CVD. The thickness of the first padlayer 40 is from about 3 nm to about 30 nm, and typically from about 5nm to about 15 nm.

A pad nitride layer 50 is deposited on the first pad layer 40, forexample, by chemical vapor deposition such as low pressure chemicalvapor deposition (LPCVD) or rapid thermal chemical vapor deposition(RTCVD). The pad nitride layer 50 may comprise silicon nitride, or otherdielectric nitride having sufficient resistance to chemical mechanicalpolishing. The thickness of the pad nitride layer 50 may be from about50 nm to about 250 nm, and typically from about 10 nm to about 20 nm.

A second pad layer 50 is formed on the pad nitride layer 50, forexample, by chemical vapor deposition such as low pressure chemicalvapor deposition (LPCVD), rapid thermal chemical vapor deposition(RTCVD), or high density plasma chemical vapor deposition (HDPCVD). Thesecond pad layer 50 may comprise silicon oxide or other semiconductoroxide providing sufficient resistance to etching during a subsequentetching of silicon nitride.

The thickness of the second pad oxide layer 60 may be from about 10 nmto about 1,000 nm. The thickness of the second oxide layer 60 depends ona target depth of a trench into the SOI substrate 8 and the nature ofetching process employed to form the trench. For example, in case thedepth of the trench to be formed, as measured from the substrate topsurface to a bottom of the trench, is from about 200 nm to about 500 nm,and a soft mask process, in which the photoresist 71 is presentthroughout the etching process, the thickness of the second pad oxidelayer may be from about 10 nm to about 100 nm. In case the depth of thetrench to be formed is from about 500 nm to about 8,000 nm, and a hardmask process, in which the photoresist 71 is consumed or removed duringthe etching process and the second pad oxide layer 60 as patterned isemployed as an etch mask, the thickness of the second pad oxide layermay be from about 50 nm to about 1,000 nm.

Referring to FIGS. 3 and 4, a photoresist 71 is applied onto the topsurface of the second pad layer and is lithographically patterned todefine active areas AA, within which semiconductor devices aresubsequently formed. FIG. 3 is a vertical cross-sectional view and

FIG. 4 is a top down view of the first exemplary semiconductorstructure. The active areas AA correspond to areas in which thephotoresist 71 remains after patterning. Typically, each of the activeareas AA is disjoined from other active areas, i.e., an area devoid ofthe photoresist 71 encloses each of the active areas AA. The complementof the set of all active areas AA, i.e., the area without thephotoresist 71, may be a single contiguous area, or may be multipledisjoined areas.

A reactive ion etch is employed to transfer the pattern in thephotoresist 71 into the stack of the second pad oxide layer 70, the padnitride layer 50, and the first pad oxide layer 40, exposing thesubstrate top surface 29 between the active areas AA. The photoresist 71may, or may not, be removed at this point depending on the depth of thetrench to be subsequently formed and the etch chemistry to be employedtherein.

Referring to FIG. 5, the pattern in the photoresist 71 or in the secondpad oxide layer 70 is transferred into the SOI substrate 8 by a reactiveion etch to a trench depth td from the substrate top surface 29 into theSOI substrate 8. The trench depth td is greater than the depth of abottom surface of the buried insulator layer 20 as measured from thesubstrate top surface 29. The trench depth d may be from about 200 nm toabout 8,000 nm. In case the complement of the set of all active areas AAis a single contiguous area, a single trench T is formed. In case thecomplement of the set of all active areas AA comprises multipledisjoined areas, a plurality of disjoined trenches is formed.Construction of a plurality of disjoined trenches requires modificationof the pattern in the photoresist 71, which is known to one of ordinaryskill in the art.

At least one top semiconductor portion 32 enclosed by the trench T isformed from remaining portions of the top semiconductor layer 30. Thecollection of all of the at least one top semiconductor portion 32constitutes the top semiconductor layer 30. At least one buriedinsulator portion 22 enclosed by the trench T is formed from remainingportions of the buried insulator layer 20. The collection of all of theat least one buried insulator layer 22 constitutes the buried insulatorlayer 20. Each of the at least one top semiconductor portion 32vertically abuts one of the at least one buried insulator portion 22.The sidewalls of each of the at least one top semiconductor portion 32and sidewalls of the buried insulator portion 22 directly underneath arevertically coincident, i.e., coincident in a vertical view such as atop-down view.

Referring to FIG. 6, a silicon nitride layer 80 is deposited in thetrench T (See FIG. 5) and on the second pad oxide layer 70. The trench Tis filled with the silicon nitride layer 80. Preferably, the siliconnitride layer 80 comprises a stress-generating silicon nitride, whichmay be the same material as stress-generating silicon nitride linersformed over a gate electrode as known in the art. Such stress-generatingsilicon nitride liners of the prior art, having a typical thickness fromabout 30 nm to about 80 nm, are known to generate compressive stress ortensile stress, of which the magnitude may exceed 0.2 GPa. Thedifference between the prior art and the present invention is that suchstress-generating silicon nitride is formed above a top surface of asemiconductor substrate over a gate electrode in the prior art, whilethe stress-generating silicon nitride is located in a trench formedbeneath the substrate top surface 29 prior to formation of any gateelectrode.

As such, the stress-generating silicon nitride may be a tensilestress-generating silicon nitride or a compressive stress-generatingsilicon nitride. The portion of the silicon nitride layer 80 within thetrench T exerts a compressive stress or a tensile stress to structuresthat the trench T encloses, which include the at least one topsemiconductor portion 32, the at least one buried insulator portion 22,and the portion of the handle substrate 10 between a bottom surface ofthe buried insulator layer 20 and a bottom surface of the trench T. Themagnitude of the compressive stress or the tensile stress may be greaterthan 0.2 GPa in a region of each of the at least one top semiconductorportion 32. In practice, the region in which the magnitude of thecompressive stress or the tensile stress exceeds 0.2 GPa may includemost of each of the at least one top semiconductor portion 32 except fora boundary region of each of the at least one top semiconductor portion32 directly on the trench T.

The thickness of the silicon nitride layer 80, as measured above thesecond pad oxide layer 70, is greater than half of the narrowestdistance in the opening of the trench T to insure complete fill of thetrench. Consequently, the thickness of the silicon nitride layer isgreater than half of the critical dimension, i.e., the minimum dimensionthat lithographic tools may print. The critical dimension is reducedwith each generation of lithographic tools, and is about 50 nm as of2007. The thickness of the silicon nitride layer 80 may be from about 25nm to about 300 nm, and preferably from about 25 nm to about 150 nm,although lesser and greater thicknesses are also explicitly contemplatedherein.

The stress-generating silicon nitride employed for the silicon nitridelayer 80 may be formed by chemical vapor deposition (CVD) such as plasmaenhanced chemical vapor deposition (PECVD), high density plasma chemicalvapor deposition (HDPCVD), rapid thermal chemical vapor deposition(RTCVD), low pressure chemical vapor deposition (LPCVD), or acombination thereof.

Referring to FIG. 7, the silicon nitride layer 80 (See FIG. 6) isrecessed below a top surface of the at least one top semiconductorportion 32. The depth of recess as measured from the top surface of theat least one top semiconductor portion 32, which is herein referred toas a nitride recess depth nrd, may be less than the thickness of the atleast one top semiconductor portion 32 so that the top surface of aninsulator stressor plug 82, which is the remaining portion of thesilicon nitride layer 80, is located between the top surface of the atleast one top semiconductor portion 32 and a bottom surface of the atleast one top semiconductor portion 32. Alternately, the nitride recessdepth nrd, may be equal to the thickness of the at least one topsemiconductor portion 32 so that the top surface of the insulatorstressor plug 82 is at the depth of the bottom surface of the at leastone top semiconductor portion 32. Even alternately, the nitride recessdepth nrd may be greater than the thickness of the at least one topsemiconductor portion 32 and less than the sum of the thickness of theat least one top semiconductor portion 32 and the thickness of the atleast one buried insulator portion 22 so that the top surface of aninsulator stressor plug 82 is located between a top surface of the atleast one buried insulator portion 22 and a bottom surface of the atleast one buried insulator portion 22. Yet alternately, the nitriderecess depth nrd, may be equal to the sum of the thickness of the atleast one top semiconductor portion 32 and the thickness of the at leastone buried insulator portion 22 so that the top surface of the insulatorstressor plug 82 is at the depth of the bottom surface of the at leastone buried insulator portion 22. Still alternately, the nitride recessdepth nrd may be greater than the sum of the thickness of the at leastone top semiconductor portion 32 and the thickness of the at least oneburied insulator portion 22 so that the top surface of an insulatorstressor plug 82 is located beneath the bottom surface of the at leastone buried insulator portion 22.

An etch process that etches the silicon nitride layer 80 selective tothe second pad oxide layer 70 is employed. Preferably, the etch processis a reactive ion etch (RIE) process in which the etch ratio between thesilicon nitride layer 80 and the second pad oxide layer 70 is high, sothat at least a portion of the second pad oxide layer 70 remains at theend of the reactive ion etch.

Referring to FIG. 8, a silicon oxide layer 90 is deposited on theinsulator stressor plug 82 in the trench T (See FIG. 5) and on thesecond pad oxide layer 70. The portion of the trench T above theinsulator stressor plug 82 is filled with the silicon oxide layer 90.

The silicon oxide layer 90 may be formed by chemical vapor deposition(CVD) such as plasma enhanced chemical vapor deposition (PECVD), highdensity plasma chemical vapor deposition (HDPCVD), rapid thermalchemical vapor deposition (RTCVD), low pressure chemical vapordeposition (LPCVD), or a combination thereof. A precursor containingsilicon and oxygen, such as tetra-ethyl-ortho-silicate (TEOS) may beemployed in the CVD process. The silicon oxide layer 90 may, or may not,comprise the same material as the second pad oxide layer 70.

The thickness of the silicon oxide layer 90, as measured above thesecond pad oxide layer 70, is greater than half of the narrowestdistance in the opening of the trench T to insure complete fill of thetrench without a void. Consequently, the thickness of the siliconnitride layer is greater than half of the critical dimension. Thethickness of the silicon oxide layer 90 may be from about 25 nm to about300 nm, and preferably from about 25 nm to about 150 nm, although lesserand greater thicknesses are also explicitly contemplated herein.

Referring to FIG. 9, the silicon oxide layer 90 is planarized bychemical mechanical polishing (CMP) employing the pad nitride layer 50as a stopping layer. Optionally, a recess etch, which may be a reactiveion etch, a wet etch, a chemical downstream etch, or any combinationthereof, may be employed in conjunction with the chemical mechanicalpolishing. Methods of performing a CMP process on a silicon oxide layeremploying a nitride layer as the stopping layer are well known in theart. The remaining portion of the silicon oxide layer 90 after the CMPstep constitutes a planarized silicon oxide layer 92. A top surface ofthe planarized silicon oxide layer 92 is substantially coplanar with atop surface of the pad nitride layer 50.

Referring to FIG. 10, the planarized silicon oxide layer 92 is recessedby a first etch that etches the planarized silicon oxide layer 92selective to the pad nitride layer 50. The first etch may be a wet etch,a reactive ion etch, a chemical dry etch, or any combination thereof. Anexemplary wet etch process is a wet etch employing hydrofluoric acid(HF), which selectively etches the planarized silicon oxide layer 92relative to the pad nitride layer 50. The remaining portion of theplanarized silicon oxide layer 92 after the etch constitutes a siliconoxide plug 94. Preferably, a top surface of the silicon oxide plug 94 islocated about the interface between the first pad oxide layer 40 and thepad nitride layer 50.

Referring to FIGS. 11-13, the pad nitride layer 50, the first pad oxidelayer 40, and a top portion of the silicon oxide plug 94 are removed.FIG. 11 is a vertical cross-sectional view of the first exemplarysemiconductor structure. FIG. 12 is a top-down view of the firstexemplary semiconductor structure in FIG. 11. FIG. 13 is a horizontalcross-sectional view of the first exemplary semiconductor structure inFIG. 11 along the plane X-X′.

Specifically, the pad nitride layer 50 is removed selective to thesilicon oxide plug 94 and the first pad oxide layer 40 by a second etch,which may be a wet etch, a reactive ion etch, a chemical dry etch, orany combination thereof. In case the pad nitride layer 50 comprisessilicon nitride, a wet etch employing hot phosphoric acid may beemployed to selectively remove the pad nitride layer 50, while notaffecting the silicon oxide plug 94 and the first pad oxide layer 40.

The first pad oxide layer 40 and a top portion of the silicon oxide plug94 may then be removed by a third etch selective to the at least one topsemiconductor portion 32. The third etch may be, for example, a wet etchemploying hydrofluoric acid (HF). Preferably, amount of removal of thetop portion of the silicon oxide plug 92 is such that a top surface ofthe silicon oxide plug 94 is substantially coplanar with the top surfaceof the at least one top semiconductor portion 32.

The first exemplary semiconductor structure of FIGS. 11-13 comprises:

a semiconductor-on-insulator (SOI) substrate 8 including a handlesubstrate 10, at least one buried insulator portion 22 abutting thehandle substrate 10, and at least one top semiconductor portion 32abutting the at least one buried insulator portion 22;

a trench extending from a top surface, which is the substrate topsurface 29, of the at least one top semiconductor portion 32, to adepth, which is the trench depth td, below a bottom surface of the atleast one buried insulator portion 22; and

a stack of an insulator stressor plug 82 and a silicon oxide plug 94located in the trench, wherein the insulator stressor plug 82 abuts abottom surface of the trench and the silicon oxide plug 94 issubstantially coplanar with the top surface, which is the substrate topsurface 29, of the at least one top semiconductor portion 32.

In the first exemplary semiconductor structure, an interface between theinsulator stressor plug 82 and the silicon oxide plug 94 is locatedbetween the top surface, which is the substrate top surface 29, of theat least one top semiconductor portion 32 and a bottom surface of the atleast one top semiconductor portion 32.

The first exemplary semiconductor structure provides a substantiallyflat top surface, which is the substrate top surface 29, over theentirety of the SOI substrate 8. Further, the substrate top surface 29comprises a semiconductor material of the at least one semiconductorportion 32 and silicon oxide of the silicon oxide plug 94. Thiscomposition is identical to the composition of a top surface of aconventional complementary metal-oxide-semiconductor (CMOS) structureafter formation of shallow trench isolation. Thus, the first exemplarysemiconductor structure may employ identical processing steps after theprocessing step of FIGS. 11-13 as conventional CMOS structures. In otherwords, the first exemplary semiconductor structure is compatible withconventional semiconductor processing sequence after the step of FIGS.11-13.

Referring to FIG. 14, a stress schematic indicating the direction ofstress generated by the insulator stressor plug 82 is shown insuperposition on the first exemplary semiconductor structure of FIG. 11for the case in which the insulator stressor plug 82 generates a tensilestress. The tensile stress is applied to the handle substrate 10 and tothe at least one top semiconductor portion 32. A semiconductor devicemay be formed in the at least one top semiconductor portion 32 such thatthe tensile stress applied to the at least one top semiconductor portion32 is advantageously utilized to enhance performance of thesemiconductor device. For example, the at least one top semiconductorportion 32 may comprise silicon and the semiconductor device may be ann-type field effect transistor having a channel in the direction of thelateral tensile stress and employing electrons as charge carriers. Inthis case, the mobility of the electrons increases as a result of thelateral tensile stress on the at least one top semiconductor layer 32.

Referring to FIG. 15, a stress schematic indicating the direction ofstress generated by the insulator stressor plug 82 is shown insuperposition on the first exemplary semiconductor structure of FIG. 11for the case in which the insulator stressor plug 82 generates acompressive stress. The compressive stress is applied to the handlesubstrate 10 and to the at least one top semiconductor portion 32. Asemiconductor device may be formed in the at least one top semiconductorportion 32 such that the compressive stress applied to the at least onetop semiconductor portion 32 is advantageously utilized to enhanceperformance of the semiconductor device. For example, the at least onetop semiconductor portion 32 may comprise silicon and the semiconductordevice may be an p-type field effect transistor having a channel in thedirection of the lateral compressive stress and employing holes ascharge carriers. In this case, the mobility of the holes increases as aresult of the lateral compressive stress on the at least one topsemiconductor layer 32.

Referring to FIG. 15, a second exemplary semiconductor structureaccording to the present invention is shown. The interface between theinsulator stressor plug 82 and the silicon oxide plug 94 is locatedbetween a top surface, which is the substrate top surface 29, of the atleast one buried insulator portion 32 and the bottom surface of the atleast one buried insulator portion 32.

Referring to FIG. 16, a third exemplary semiconductor structureaccording to the present invention is shown. The interface between theinsulator stressor plug 82 and the silicon oxide plug 94 is locatedbeneath the bottom surface of the at least one buried insulator portion22.

Embodiments in which the interface between the insulator stressor plug82 and the silicon oxide plug 94 is located at the bottom surface of theat least one top semiconductor portion 32 or at the bottom surface ofthe at least one buried insulator portion 22 are explicitly contemplatedherein.

Referring to FIG. 18, a two-dimensional model for simulation of stressin a fourth exemplary semiconductor structure according to the presentinvention. In this two-dimensional model, the structure of the fourthexemplary semiconductor in the direction perpendicular to the plane ofthe model, i.e., the plane of FIG. 18, is assumed to continueindefinitely, i.e., sufficiently long enough not to affect the resultsof the simulation.

The cross-sectional area of a handle substrate 10 (See FIG. 11) isapproximated by a handle substrate area 110. The cross-sectional area ofan insulator stressor plug 82 (See FIG. 11) is approximated by aninsulator stressor plug area 182. The cross-sectional area of at leastone buried insulator portion 22 (See FIG. 11) is approximated by atleast one buried insulator portion area 122. The cross-sectional area ofat least one top semiconductor portion 32 (See FIG. 11) is approximatedby at least one top semiconductor portion area 132. The effect of asilicon oxide plug 94 is assumed to be insignificant, and a void area199 was introduced in the area of the silicon oxide plug 94. In thistwo-dimensional model, a top surface of the insulator stressor plug area182 is located at the bottom surface of the at least one topsemiconductor portion area 132. The insulator stressor plug area 182 isassumed to have the same property as one of tensile silicon nitridematerial known in the art.

FIG. 19 is a plot of lateral stress from a simulation employing thetwo-dimensional model of FIG. 15. Lateral tensile stress up to about 1.8GPa is observed in the at least one top semiconductor portion area 132.In most regions of the at least one top semiconductor portion area 132,the lateral tensile stress is greater than 0.5 GPa. The magnitude of thelateral tensile stress falls below 0.5 GPa only near the boundary withthe insulator stressor plug area 182 (See FIG. 18). Thus, the magnitudeof the tensile stress may be greater than 0.5 GPa in a region in the atleast one top semiconductor portion 32 in the exemplary semiconductorstructures demonstrated above.

While the present invention has been particularly shown and describedwith respect to preferred embodiments thereof, it will be understood bythose skilled in the art that the foregoing and other changes in formsand details may be made without departing from the spirit and scope ofthe present invention. It is therefore intended that the presentinvention not be limited to the exact forms and details described andillustrated, but fall within the scope of the appended claims.

1. A semiconductor structure comprising: a semiconductor-on-insulator(SOI) substrate including a handle substrate, at least one buriedinsulator portion abutting said handle substrate, and at least one topsemiconductor portion abutting said at least one buried insulatorportion; a trench extending from a top surface of said at least one topsemiconductor portion to a depth below a top surface of said at leastone buried insulator portion; and a stack of an insulator stressor plugand a silicon oxide plug located in said trench, wherein said insulatorstressor plug abuts a bottom surface of said trench and said siliconoxide plug is substantially coplanar with said top surface of said atleast one top semiconductor portion, wherein an interface between saidinsulator stressor plug and said silicon oxide plug is located betweensaid top surface of said at least one top semiconductor portion and abottom surface of said at least one top semiconductor portion, or atsaid bottom surface of said at least one top semiconductor portion. 2.The semiconductor structure of claim 1, wherein said insulator stressorplug comprises a silicon nitride and applies a tensile stress or acompressive stress to said at least one top semiconductor portion. 3.The semiconductor structure of claim 2, wherein a magnitude of saidtensile stress or said compressive stress is greater than 0.2 GPa in aregion in said at least one top semiconductor portion.
 4. Thesemiconductor structure of claim 1, wherein said insulator stressor pluglaterally abuts, and encloses, said at least one buried insulatorportion.
 5. The semiconductor structure of claim 4, wherein saidinsulator stressor plug laterally abuts and encloses said at least onetop semiconductor portion.
 6. The semiconductor structure of claim 1,wherein said at least one top semiconductor layer comprises one ofsilicon, germanium, a silicon germanium alloy, a silicon carbon alloy,and a silicon germanium carbon alloy.
 7. The semiconductor structure ofclaim 1, wherein a thickness of said at least one top semiconductorportion is from about 5 nm to about 300 nm, and wherein a depth of saidtrench is from about 200 nm to about 8,000 nm.
 8. A semiconductorstructure comprising: a semiconductor-on-insulator (SOI) substrateincluding a handle substrate, at least one buried insulator portionabutting said handle substrate, and at least one top semiconductorportion abutting said at least one buried insulator portion; a trenchextending from a top surface of said at least one top semiconductorportion to a depth below a top surface of said at least one buriedinsulator portion; and a stack of an insulator stressor plug and asilicon oxide plug located in said trench, wherein said insulatorstressor plug abuts a bottom surface of said trench and said siliconoxide plug is substantially coplanar with said top surface of said atleast one top semiconductor portion, wherein an interface between saidinsulator stressor plug and said silicon oxide plug is located between atop surface of said at least one buried insulator portion and saidbottom surface of said at least one buried insulator portion, or at saidbottom surface of said at least one buried insulator portion, or theinterface between said insulator stressor plug and said silicon oxideplug is located beneath said bottom surface of said at least one buriedinsulator portion.
 9. The semiconductor structure of claim 8, whereinsaid insulator stressor plug comprises a silicon nitride and applies atensile stress or a compressive stress to said at least one topsemiconductor portion.
 10. The semiconductor structure of claim 8,wherein a magnitude of said tensile stress or said compressive stress isgreater than 0.2 GPa in a region in said at least one top semiconductorportion.
 11. The semiconductor structure of claim 8, wherein saidinsulator stressor plug laterally abuts, and encloses, said at least oneburied insulator portion.
 12. The semiconductor structure of claim 11,wherein said insulator stressor plug laterally abuts and encloses saidat least one top semiconductor portion.
 13. The semiconductor structureof claim 8, wherein said at least one top semiconductor layer comprisesone of silicon, germanium, a silicon germanium alloy, a silicon carbonalloy, and a silicon germanium carbon alloy.
 14. The semiconductorstructure of claim 8, wherein a thickness of said at least one topsemiconductor portion is from about 5 nm to about 300 nm, and wherein adepth of said trench is from about 200 nm to about 8,000 nm.
 15. Amethod of forming a semiconductor structure comprising: proving asemiconductor-on-insulator (SOI) substrate including a top semiconductorlayer and at least one buried insulating layer, wherein said at leastone buried insulator layer vertically abuts said at least one topsemiconductor layer; forming a trench extending from a top surface of asemiconductor-on-insulator (SOI) substrate to a depth beneath a bottomsurface of a buried insulator layer of said SOI substrate, wherein saidtrench laterally abuts and encloses at least one top semiconductorportion formed in a top semiconductor layer of said SOI substrate; andforming a stack of an insulator stressor plug and a silicon oxide plugin said trench, wherein said insulator stressor plug abuts a bottomsurface of said trench, and wherein said silicon oxide plug issubstantially coplanar with a top surface of at least one topsemiconductor portion formed in a top semiconductor layer of said SOIsubstrate, wherein an interface between said insulator stressor plug andsaid silicon oxide plug is located between a top surface of said atleast one top semiconductor portion and a bottom surface of said atleast one top semiconductor portion, or the interface is located at saidbottom surface of said at least one top semiconductor portion, or theinterface is located between a top surface of said buried insulatorlayer and said bottom surface of said buried insulator layer, or at saidbottom surface of said buried insulator layer.
 16. The method of claim15, further comprising: forming a stack of pad layers directly on saidSOI substrate; applying a photoresist on said stack of pad layers andlithographically patterning said photoresist; and transferring a patternin said resist into said stack of pad layers and said SOI substrate byat least one reactive etch.
 17. The method of claim 15, furthercomprising: depositing a silicon nitride into said trench; and recessingsaid silicon nitride in said trench to form said insulator stressorplug.
 18. The method of claim 15, wherein said insulator stressor plugcomprises a silicon nitride and applies a compressive stress or atensile stress to said at least one top semiconductor portion.
 19. Themethod of claim 15, further comprising: depositing a silicon oxide intosaid trench on top of said insulator stressor plug; and recessing saidsilicon oxide in said trench to form said silicon oxide plug.
 20. Themethod of claim 15, wherein a thickness of said at least one topsemiconductor portion is from about 5 nm to about 300 nm, and wherein adepth of said trench is from about 200 nm to about 8,000 nm.